• Vinyl Chloride and Vinyl Acetate Copolymers MLC-10-80
  • Vinyl Chloride and Vinyl Acetate Copolymers MLC-10-80

Vinyl Chloride and Vinyl Acetate Copolymers MLC-10-80

Inquire Now Next Product
Product Details

New grade MLC-10-80: It is white powder,ester soluble with colorless, transparent solution, and it has with very good dissoluvability、film-formation 、color contrast property 、solvent release property、high hardness、high tenacity、high chemical resistance、pulling and tearing resistance; It has lasting flexibility、abrasive resistance、low expansion rate and low water and gas permeability, therefore, it can be oil resistivity、grease resistance、dilute acid resistance、alkali resistance、salt resistance and alcohol resistance. It is also is binders with physical property drying with the film formation after the solvent volatilization in the system.

MLC-10-80 Vinyl Resin Quality standard (XHQB-6)

No.ItemIndexTest method
1AppearanceWhite powderBy visual
3Composition % by WtVinyl Chloride 90±1%GB/T7139-2002
Vinyl Acetate 10±1%ISO1159-1978
4Reactive Functionality Type % by Wt-
5K Value58-60GB/T 3401-2007
6Viscosity No. ml/g82-88GB/T 3401-2007
7Glass Transition Temp ℃About 79GB11998-89
8Average Molecular WtAbout 44000Calculated by the Viscosity No.
9% by wt, through 50 mesh100%GB/T6003.1
10Apparent density (g/ml)≥0.5GB20022-2005
11Volatilization (%)≤1%GB/T2914-1999
12Impurity Particle No. /100g≤20GB9348-88
1315% resin in MEK or EAColorless and TransparentBy visual


MLC-10-80 new grade is used for application strippable coating、screen printing ink 、PVC Printing ink、UPVC Pipe binder、PVC internal plasticization、paper coating 、plasticizer shielding coatings etc

Package, storage and transportation:

* In kraft bag, lined with pp bags of 25kgs net, with PE inner bag.

*Store in a dry and ventilated place, do not place in open-air, avoid storage in direct sunlight and caution against wet.

*Must be transported in clean vehicle with awning and keep away from moisture.

* It is NOT hazardous article, and the shelf life is one year from the production date.